Method of synthesizing tungsten carbide nanorods and catalysts formed therewith

ABSTRACT

A method of synthesizing tungsten carbide nanorods, the method comprising: mixing tungsten oxide (WO 3 ) nanorods with a carbon source to obtain precursors; and calcining the precursors to obtain tungsten carbide nanorods, without use of any catalyst. A catalyst of metal nanostructures supported on tungsten carbide nanorods.

FIELD OF THE INVENTION

This invention relates to a method of synthesizing tungsten carbidenanorods and catalysts formed therewith, in particular, to synthesis ofhigh surface area tungsten carbide nanorods forcatalysis/electrocatalysis applications.

BACKGROUND OF THE INVENTION

In recent years, tungsten carbide (WC) has attracted considerableattention for catalytic and electro-catalytic applications since thediscovery of its Pt-like characteristics as reported by Levy andBoudart.¹ It is well known that WC has high catalytic activity forhydrogenolysis and isomerization reactions.²⁻⁷ Tungsten carbide is alsoreported to exhibit certain activity for many electrochemical reactionsof interest, including hydrogen oxidation,^(8, 9) oxygenreduction,^(10, 11) hydrogen evolution reaction (HER),¹² and oxidationof various organic molecules.⁹ Although its electro-catalytic activitywas usually not sufficient, the low cost and insensitivity to catalystpoisons such as CO make it an interesting alternative to noble metalcatalyst. Other than direct use as a catalyst, tungsten carbide has alsobeen intensively studied as a catalyst support for variousreactions.^(10, 13-15) Particularly, its high corrosion resistance andsuperior electronic conductivity renders WC suitable as anelectro-catalyst support for various electrochemical applications, suchas fuel cells.¹⁶⁻¹⁸ For example, higher catalytic activity has beenreported for Pt/WC compared to Pt/C due to the synergistic effectbetween Pt and WC.^(19, 20)

Also, sustainable hydrogen production through splitting of water hasattracted great scientific interest in the past decades.^(34, 35) Byfar, extensive research efforts have been made in developing advancedelectrocatalysts with reduced overpotential for hydrogen evolutionreaction (HER).³⁶⁻⁴² Typically, electrocatalytic system for hydrogenevolution incorporates noble metals such as platinum (Pt) because oftheir high electroactivity. However, the high cost and scarcity of noblemetals are serious barriers for their wide use in the waterelectrolysis.⁴³

Conventionally, several routes have been adopted to synthesize WCpowder, including direct carburization of tungsten or W-containingcompounds at high temperature (typically, higher than 1400° C.), solidstate metathesis and mechanical milling. However, these approaches oftenlead to low specific surface area, large particle size and poormorphology control. Commercial WC and WC synthesized by reported methodsare normally lower than 10 m² g⁻¹ and the maximum value reported is ˜100m² g⁻¹.^(11, 21-29) To synthesize nanostructured WC with high surfacearea and controlled morphology still remains a challenge.^(30, 31)Furthermore, the ability to control specific nanostructure is criticalfor the tuning of its physical and chemical property, especially when WCis to be used as catalyst support.

SUMMARY OF INVENTION

Among various nanostructures, nanorods of WC is of particular interestdue to their unique properties and are the main objective of this work.Pseudomorphic transformation has been investigated for the synthesis ofthree-dimensionally ordered macroporous tungsten carbide from thetungsten oxide.³²

The invention is a method to synthesize a unique nanorod-structuredmesoporous tungsten carbide (denoted as m-NRTC) material with highspecific surface area of 198 m² g⁻¹ by pseudomorphic transformation ofchemically synthesized WO₃ nanorods. This method combines asize-controlled hydrothermal reaction and a thermal treatment in thepresence of chemically synthesized WO₃ and glucose. A newelectro-catalyst composed of Pt nanoparticles supported on m-NRTC isalso synthesized and demonstrated using methanol electro-oxidation andCO stripping. The new electro-catalyst demonstrates higherelectro-catalytic activity for methanol electro-oxidation, bettertolerance to CO poisoning and superior hydrogen evolution reaction thana Pt/C catalyst. This work provides a simple and economic thought tosynthesize nanorod-structured WC materials by preparing oxide precursorswith the desired external morphology, thus leading to more applicationsof those materials in the related reaction systems.

The present invention thus significantly improves the utilization andthe catalytic efficiency of WC materials with smaller particles size andcontrolled morphology by pseudomorphic transformation of chemicallysynthesized WO₃ nanorods. Also, the synthesis of m-NRTC materials withhigh uniformity, high specific surface areas and nano-size as specifiedin the present invention is important for developing it as theelectrocatalysts as well as catalyst support that exhibit a synergisticeffect with Pt.

According to a first aspect, there is provided a method of synthesizingtungsten carbide nanorods, the method comprising: mixing tungsten oxide(WO₃) nanorods with a carbon source to obtain precursors; and calciningthe precursors to obtain tungsten carbide nanorods, without use of anycatalyst.

The carbon source may comprise glucose and the mixing may compriseforming a mixture of tungsten oxide (WO₃) nanorods with the glucose, themethod further comprising hydrothermally treating the mixture andevaporating the hydrothermally treated mixture prior to the calcining.

The hydrothermally treating may be performed in an autoclave at about110° C. to 300° C.

The hydrothermally treating may be performed for about 4 to 12 hours.

The calcining may comprise heating the precursors at about 600° C. to1000° C. under a flow of gas comprising at least one of: hydrogen andargon.

The calcining may be performed for about 1 to 6 hours.

The gas may comprise hydrogen and argon having a respective volume ratioof 1:3.

The flow of gas may be at a rate of about 300 mL/min.

The molar ratio of tungsten to carbon in the mixture may be 0.078.

The precursors may comprise carbon-coated tungsten oxide (WO₃) nanorods.

Alternatively, the carbon source may comprise methane and the mixing maycomprise heating the tungsten oxide (WO₃) nanorods in the presence ofthe methane and hydrogen in a furnace.

According to a second aspect, there is provided tungsten carbidenanorods synthesized according to the method of the first aspect.

The tungsten carbide nanorods may have a mesoporous structure.

The tungsten carbide nanorods may have a specific surface area greaterthan or equal to 170 m² g⁻¹.

According to a third aspect, there is provided a method of synthesizinga catalyst of metal nanostructures supported on tungsten carbidenanorods, the method comprising: mixing tungsten oxide (WO₃) nanorodsand a carbon source to obtain precursors; calcining the precursors toobtain tungsten carbide nanorods, without use of any catalyst; anddepositing metal nanostructures on the tungsten carbide nanorods to formthe catalyst.

The metal nanostructures may comprise platinum nanoparticles and thedepositing may comprise: suspending the tungsten carbide nanorods inethylene glycol to form a solution; adding hexachloroplatinic acid tothe solution; and drying a solid in the solution to form the catalyst.

Suspending the tungsten carbide nanorods in ethylene glycol may compriseultrasonic stirring.

The hexachloroplatinic acid may be added dropwise to the solution toreach a concentration of 4.6 mg platinum per millilitre of ethyleneglycol.

The method of the third aspect may further comprise increasingalkalinity comprises adding sodium hydroxide to adjust the pH of thesolution to above 13.

The method of the third aspect may further comprise filtering andwashing the solid prior to the drying.

The drying may be performed in a vacuum oven at about 25° C. to 100° C.

The method of the third aspect may further comprise increasingalkalinity of the solution prior to the drying.

The method of the third aspect may further comprise heating the solutionto reduce platinum in the solution prior to the drying.

The heating may be at about 100° C. to 200° C.

The method of the third aspect may further comprise promoting with asedimentation promoter adsorption of suspended platinum nanoparticlesonto the tungsten carbide nanorods prior to the drying.

Alternatively, the metal nanostructures may comprise at least oneselected from the group consisting: of Pd, Ag and Rh.

According to a fourth aspect, there is provided a catalyst of metalnanostructures supported on tungsten carbide nanorods.

The metal nanostructures may comprise platinum nanoparticles and whereinthe catalyst is synthesized according to the method of the third aspect.

The catalyst may have a mesoporous nanorod structure comprisingmesopores among aggregated nanorods.

The catalyst may have a higher electro-catalytic activity for methanolelectro-oxidation than a catalyst of platinum nanoparticles on a carbonsupport.

The catalyst may have a greater tolerance to carbon monoxide poisoningthan a catalyst of platinum nanoparticles on a carbon support.

BRIEF DESCRIPTION OF FIGURES

In order that the invention may be fully understood and readily put intopractical effect there shall now be described by way of non-limitativeexample only exemplary embodiments of the present invention, thedescription being with reference to the accompanying illustrativedrawings.

FIG. 1 is a schematic illustration of formation of m-NRTC;

FIG. 2 shows XRD patterns of m-NRTC samples synthesized at two differenttemperatures 800° C. and 900° C. with molar ration of WO₃ to glucose of0.078 with the reaction time of 3 h;

FIGS. 3 a, 3 b and 3 c are FESEM and TEM images of m-NRTC;

FIGS. 4 a, 4 b and 4 c ar TEM images of as prepared Pt/m-NRTC and Pt/Ccatalysts;

FIG. 5 shows nitrogen adsorption/desorption isotherms of m-NRTC withinset being a pore size distribution curve;

FIG. 6 a shows cyclic voltagrammograms of methanol oxidation on m-NRTC,Pt/C and Pt/m-NRTC in 0.5 mol L⁻¹ H₂SO₄+1 mol L⁻¹ CH₃OH solution, scanrate: 50 mV s-1;

FIG. 6 b shows CO-stripping results on m-NRTC, Pt/C and Pt/m-NRTC in a0.5 mol L⁻¹H₂SO₄ aqueous solution, scan rate: 15 mVs⁻¹;

FIG. 7 shows cyclic voltammograms hydrogen evolution reaction on WCnanorods, Pt/C and Pt/WC-rods in 100 mM H₂SO₄, scan rate: 5 mVs⁻¹;

FIG. 8 shows cyclic voltammograms of Pt supported on WC-nanorods andMWCNTs before and after potential sweep for 2000 cycles in 0.5 M H₂SO₄;

FIG. 9 shows polarization curves of Pt catalysts supported onWC-nanorods and MWCNTs before and after potential sweep for 2000 cyclesin 0.5 M H₂SO₄; and

FIG. 10 shows cyclic voltammograms of hydrogen evolution reaction on WCnanorods, Pt/C and Pt/WC-rods in 100 mM pH 7, phosphate buffer, scanrate: 5 mV s⁻¹.

DETAILED DESCRIPTION

Exemplary embodiments of the invention will be described with referenceto FIGS. 1 to 10 below.

Synthesis of WO₃ Nanorods

In a typical or exemplary method of synthesis, 0.6597 g of Na₂WO₄.₂H₂O(Sigma-Aldrich) and 0.5286 g of (NH₄)₂SO₄ (Sigma-Aldrich) were dissolvedin 15 ml de-ionized water, then 3M HCl (Sigma-Aldrich) aqueous solutionwas added to adjust the pH value to 2.0.

Afterwards, the solution obtained was transferred into a Teflon-linedstainless autoclave where the reaction was maintained at 180° C. for 8h. Then the precipitate was filtered, washed sequentially with water andethanol, and dried at 60° C. to obtain as-prepared WO₃ nanorods 10.

Synthesis of m-NRTC and m-WC

As shown in FIG. 1, in a typical or exemplary synthesis procedure ofm-NRTC 40, a proper amount of the as-prepared WO₃ nanorods 10 andglucose (Sigma-Aldrich) (the molar ratios of W: C=0.078) were dissolvedin 15 mL distilled-deionized water and vigorously stirred for 20 min.The mixture was hydrothermally treated in a sealed Teflon linedstainless steel autoclave at a temperature of between 110° C. to 300° C.(e.g. 180° C.), for about 4 to 12 hours (e.g. 8 hours) to obtaincarbon-coated WO₃ nanorods 20 that subsequently underwent evaporation toform m-NRTC precursors 30 of the m-NRTC. The as-prepared precursors 30were calcined at about 600° C. to 1000° C. (e.g. 900° C.) under a flowof H₂/Ar (V_(H) ₂ /V_(Ar)=1:3, 300 mL/min) for 3 hours in a tube furnaceto finally form m-NRTC 40.

Since no catalysts such as Mg have been used in the above synthesis, noby-products such as MgWO₄ or any precursors of WO₃ remain. The finalproduct arising from the synthesis method 100 of the present inventionis only WC nanorods with a very thin graphite carbon film of about 1 nmthickness, or m-NRTC.

Instead of using glucose which acts as a solid carbon source in themethod of synthesis described above, a gaseous source of carbon such asmethane (CH₄) may be used to synthesize the tungsten carbide nanorods.Where methane is used, the obtained tungsten carbide nanorods ismesoporous WC (m-WC) with high purity, that is, no obvious carbondetected by currently available devices.

In an exemplary method of synthesis of m-WC using methane as the carbonsource, a certain amount (e.g. 50 to 80 mg) of the as-prepared WO₃nanorods is transferred into a tube furnace for reduction-carburization.The whole system should be airproofed and an inert gas such as argon maybe used to completely remove any ambient air before heating the tubefurnace. Subsequently, the argon is switched off and replaced with amixture of CH₄ at an exemplary flow rate of 20 mLmin⁻¹ and H₂ at anexemplary flow rate of 80 mLmin⁻¹. In the meantime, the tube furnace isheated to 600° C. with a ramp rate of 5° C. min⁻¹ to obtain precursorsof the m-WC. Subsequently, the tube furnace is heated to 800° C. at arate of 2° C. min⁻¹ and kept at this temperature for 3 h with the samecarburizing agent comprising the methane and hydrogen gas mixturedescribed above, thereby calcining the precursors of the m-WC. It isalso important to appreciate that in this embodiment, the calcining isperformed for about between 1 to 6 hours. When the tube furnace hascooled down to a temperature of 700° C., the carburizing agent isswitched off and the inert gas such as argon is again switched on. Thetube furnace is further cooled down to room temperature to obtain them-WC prepared using methane as the gaseous carbon source.

Preparation of Pt/m-NRTC and Pt/C Catalysts

Pt/m-NRTC and Pt/C catalysts were synthesized by an Ethylene Glycol (EG)method. These catalysts comprise Pt nanoparticles on either m-NRTC orcarbon support. Briefly, 40 mg of m-NRTC or XC-72 carbon powder (Gashub)were suspended in 10 mL of ethylene glycol solution (Sigma-Aldrich) andstirred with ultrasonic treatment for 30 min; 2.2 mL ofhexachloroplatinic acid (Sigma-Aldrich) EG solution (4.6 mg Pt/mL EG)was added to the solution dropwise also under mechanically stirredconditions for 3 h. NaOH (Fluka) (2 M in EG solution) was added toadjust the pH of the solution to above 13, and then the solution washeated at about 100° C. to 200° C. (e.g. 140° C.) for 3 h to ensure thatPt was completely reduced. Thereafter, in order to promote theadsorption of suspended Pt nanoparticles onto the m-NRTC or carbonsupport, hydrochloric acid was adopted as the sedimentation promoter.The resulting black solid sample was filtered, washed and dried at about25° C. to 100° C. (e.g. 60° C.) overnight in a vacuum oven.

Characterization and Electrochemical Measurements X-Ray Diffraction(XRD) Characterization

X-ray diffraction was used to study the structure of the obtainedsamples. As shown in FIG. 2, at a constant molar ratio (0.078) of WO₃ toglucose and reaction time (3 h), the temperature plays an importantrole. With the increasing of the reaction temperature, a phasetransition was observed from W to WC as shown in FIG. 2. Based on thisresult, the optimal reaction temperature of 900° C. was determined andused to prepare WC for further characterization and measurements.

FESEM and TEM Characterization

The morphology of m-NRTC was studied by a field emission scanningelectron microscopy (FESEM, JEOL JSM 6700F). The size and morphology ofPt/m-NRTC and Pt/C catalysts were investigated by JEOL 3010 transmissionelectron microscope. It can be seen in FIG. 3 that the m-NRTC obtainedwith chemically synthesized WO₃ nanorods at the optimized temperatureshows an interesting mesoporous nanorod-structure (lengths over 300 nmto 1.0 um diameter from 50 to 70 nm), as can be seen in FIGS. 3 b and 3c, with mesopores among the aggregated nanorods, as can be seen in FIG.3 a. The synthesized NRTC powder almost kept the morphology of the asprepared WO3 precursor on a sub-100 nm length scale. From a distance theproducts show a number of large irregular mesoporous particles in FIG. 3a. At close observation, those irregular particles consist of small anduniformed nanorods as can be seen in FIGS. 3 b and 3 c because of theaggregation.

It is found from the TEM images in FIG. 4 that the Pt nanoparticles canbe uniformly dispersed on the surface of m-NCTC with an average particlesize of 4 nm.

Liquid Nitrogen Adsorption/Desorption Characterization

The BET specific surface area and pore size distribution of the m-NRTCwas measured in Autolab-6B (Quantachrome Instruments) using the liquidnitrogen adsorption method. As shown in FIG. 5, nitrogenadsorption/desorption isotherms with a distinct hysteretic loop at therelative pressure of P/P0 ranging from 0.5 to 0.9 are identified as TypeIV characteristic of mesoporous materials. The sample has a BET surfacearea of 198 m² g⁻¹ with a total pore volume of 0.30 cm³ g⁻¹, exhibitinga high specific surface area in contrast to less than 20 m² g⁻¹ forcommercial WC products and those synthesized by other methods. The poresize distribution was investigated by the Barrett-Joyner-Halenda (BJH)method. The average pore size was about 5.9 nm in m-NRTC (inset of FIG.5).

Electrochemical Measurements

Cyclic voltagrammograms of methanol oxidation on m-NRTC, Pt/C andPt/m-NRTC were measured in nitrogen purged 0.5 mol L⁻¹ H₂SO₄+1 mol L⁻¹CH₃OH solution as shown in FIG. 6 a; this represents the half-cell anodereaction of DMFC. The main feature in the CV between 0.4 V and 0.9Vrepresents oxidation/reduction of methanol (CH₃OH+H₂O→CO₂+6H⁺+6e⁻). Theobtained CV curve (curve 3 of FIG. 6 a) exhibits very prominentcharacteristic peaks for the methanol oxidation. In comparison, CVcurves of the methanol oxidation for carbon supported Pt catalyst (curve2 of FIG. 6 a) and m-NRTC (curve 1 of FIG. 6 a) were measured in thesame electrolyte used for Pt/m-NRTC. The results clearly indicate thatm-NRTC has no characteristic peaks of methanol oxidation and Pt/C has asignificantly lower electro-catalytic peak current than Pt/m-NRTC. Themain reason for this important improvement on the Pt catalyst is thatm-NRTC as the support material could significantly reduce the unitloading amount to achieve the same performance as the conventional Pt/C.As is known, a porous electrode has high internal surface area for highelectrochemical rates per apparent unit surface area of electrode.However, its internal area generally cannot be completely utilized athigh current densities due to the difficult mass transfer and ohmicpolarization in the internal pores that is simply dependant on the porestructure. Based on the porous electrode theory, a higher peak currentproduced by Pt/m-NCTC possibly indicates that the nanorod structure hasmuch higher utilization efficiency than carbon pore structure althoughthe carbon has higher specific surface area. The nanorod structure verylikely ascribes to its higher electro-activity as the mesoporousparticles composed of aggregated WC nanorods could result in someinterstices among the aggregated nanorod domain. This kind ofmicrostructure allows sufficient reactant molecule to be intercalatedinto the WC nanorods.

As shown in FIG. 6 b, the CO-stripping results on m-NRTC, Pt/C andPt/m-NRTC in a 0.5 mol L⁻¹ H₂SO₄ aqueous solution, it is shown that themore active Pt/m-NRTC gave smaller CO oxidation. The reason could be thepresence of WC reduces the adsorption of CO on the electro-catalyst.Meanwhile, it also can be seen from FIG. 6 b that CO oxidation potentialfor Pt/m-NRTC is 0.58 V vs. SCE, which is over 100 mV more negative thanthat of Pt/C (FIG. 6 b). This demonstrates the improved COelectro-oxidation activity of the Pt/m-NRTC catalyst for the CO formedduring the reaction process could be oxidized more easily at a lowerpotential on Pt/m-NRTC, thus improving the resistance to CO poisoning onthe Pt based catalyst. This is an important point as it suggests that COelectro-oxidation activity can be improved by replacing the carbonsupport with WC, which is much cheaper than Ru. It is also observed thatthe pure m-NRTC is inactive for the CO oxidation as shown in FIG. 6 b.

The potential application of this material for hydrogen evolutionreaction under acidic condition was also examined and compared to Pt/C(FIG. 7). FIG. 7 clearly shows that WC nanorods itself shows certainactivity towards hydrogen evolution reaction, which is slightly higherthan Vulcan XC-72 carbon black. After the deposition of Ptnanoparticles, Pt/WC-rods again produces higher cathodic current ofhydrogen evolution compared to Pt/C. Similar trends of catalyticactivities of tungsten carbide supported Pt catalysts have beenreported. Other than the intrinsic activity due to WC nanorods, afavorable interaction between tungsten carbides and Pt has been proposedfor the observed high current density. This demonstrates the double roleof nanostructured WC rods that works not only as the electrocatalyst butalso as catalyst support.

Comparison of Pt/WC-Nanorod Catalyst with Pt/MWCNT Catalyst

20% Pt/WC-nanorod catalyst were compared with 20% Pt/MWCNT catalyst inmainly two aspects, i.e. active surface area loss and HER stability.These catalysts comprise Pt nanoparticles on a support of eitherWC-nanorods or multi-walled carbon nanotubes (MWCNT). The results aresummarized in Table 1 below.

For active surface area loss [a], the data was collected from hydrogenadsorption/desorption peaks between 0.04 and 0.4 V as shown in FIG. 8.Durability [b] of the catalysts for HER is calculated from the activityremains after 2000 cycles at −0.05V from FIG. 9. The difference will beeven bigger if lower potential was used.

TABLE 1 Active surface area Stability for Catalysts loss ^([a]) HER^([b]) Pt/WC-nanorods 22.6% 90.0% Pt/MWCNTs 76.3% 71.9%

From the results shown in Table 1, since similar Pt nanoparticles wereused while varying only the support between WC-nanorods and MWCNT, itcan be concluded that the observed activity difference is basically dueto the effect of the support. The catalyst using WC-nanorod support showa significantly greater stability for HER than the catalyst using MWCNTsupport, while seeing significantly less active surface area loss.

Influence of pH on the Performance of MECs

The microbial electrolysis cell (MEC) cathode pH influences theperformance of a typical MEC, which depends on MEC design. In MECswithout a membrane, HER catalysts typically work around neutral pH (i.e.wastewater pH). Around neutral pH, there is a low concentration of H⁺and OH⁻ and therefore, the HER is easily transport limited, whichresults in a considerable concentration overpotential. Buffers canovercome this transport limitation, but this strongly depends on pH,buffer pKa and concentration, current density, and hydrodynamicconditions. In MECs with a membrane, the transport of cations other thanprotons through the membrane causes an increased catholyte pH, and thusHER catalysts typically work at mild alkaline pH (pH>12). At alkalinepH, the HER is not mass transport limited, and thus no buffer isrequired, but the MEC suffers from voltage losses that arise from the pHgradient between anode and cathode. As the performance of variouscatalysts under typical cathode conditions (e.g. pH) is relevant, thus,choosing the right HER catalysts for MECs is another challenge whichcannot be ignored.

Based on the above information, WC nanorods-based catalysts have beenmeasured to check their hydrogen evolution activity in a neutral pHenvironment. The data collected is shown in FIG. 10 which illustratesthe hydrogen evolution behavior of Pt supported on m-NRTC, in comparisonto pure m-NRTC, and Pt supported on XC-72 carbon at neutral pH. Bycomparison, the performance of all the materials studied is considerablylower than when under acidic conditions. This result has been expectedand reported for the cathode oxygen reduction under microbial fuel cellcondition³³. However, when compared to the acidic conditions, thesynergistic effect of m-NRTC with Pt is much more significant, thecurrent value of HER reached 6.3 times that of pure m-NRTC at the samereaction condition, and is slightly higher than that of Pt/C. It maythus be speculated that the kinetics of hydrogen evolution reaction atneutral pH is less hampered using Pt supported on m-NRTC.

Applications

As the global supply of fossil fuels predictably diminishes, fuel cells(eg. PEMFC and DEMFC) have aroused great interest as clean and efficientpower generation. While there exist many types of fuel cells eachrequiring different electrocatalysts and fuels, systems involving theoxidation of methanol to obtain hydrogen fuel or electrons appear toexhibit potential advantages over others. Currently, the electrocatalystof choice for the DMFC system is the bimetallic system of Pt/Ru;however, the Pt/Ru system is disadvantageous in terms of itsprohibitively high costs and its susceptibility to be poisoned by CO.Then tungsten carbide (WC) have become a highly potential material andbeen studied since its reported Pt-like characteristics. The objectiveof this present invention is to significantly improve the utilizationand the catalytic efficiency of WC materials with smaller particles sizeand controlled morphology by pseudomorphic transformation of chemicallysynthesized WO₃ nanorods. Also, the synthesis of m-NRTC materials withhigh uniformity, high specific surface areas and nano-size as specifiedin the present invention is important for developing it as theelectrocatalysts as well as catalyst support that exhibit a synergisticeffect with Pt.

In conclusion, described above is a method to synthesize a uniquenanorod-structured mesoporous tungsten carbide (denotes as m-NRTC) withhigh specific surface areas in the presence of chemically synthesizedWO₃ nanorods and glucose, which were used as tungsten source and carbonsource, respectively. In this method, novel carbon coated WO₃ nanorodsserved as the precursors. This way of introducing carbon within tungsticoxide maximizes the reaction rate between the reactants by improving thecontact area between the WO₃ and carbon and providing a betterdistribution of carbon within WO₃, the carbothermal reaction typicallyproceeds through reduction to W via the formation of owner oxides oftungsten, followed by carburization into WC.

The phase transition can be demonstrated according to the followingsteps:

WO3→W→W₂C→WC

The typical X-ray diffraction (XRD) patterns of the as-prepared m-NRTCsample show that at the optical conditions (molar ratio of WO₃ toglucose 0.078, reaction time 3 h and temperature 900° C.), the obtainedproducts is a pure phase of WC. FESEM results show that the obtainedm-NRTC shows an interesting mesoporous nanorod-structure (lengths over300 nm to 1.0 um diameter from 50 to 70 nm.) with mesopores among theaggregated nanorods. The synthesized NRTC powder almost kept themorphology of the as prepared WO₃ precursor on a sub-100 nm lengthscale. The Brunauer-Emmett-Teller (BET) surface area measurementconfirms the sample has a much high BET surface area of 198 m² g⁻¹ witha total pore volume of 0.30 cm³ g⁻¹. The electrochemicallycharacterization of Pt supported on m-NRTC (Pt/m-NRTC) demonstrateslarger apparent electro-catalytic current, higher electro-catalyticactivity for electrochemical oxidation of methanol and better resistanceto CO poisoning than a Pt/C catalyst.

In contrast to the less than 20 m² g⁻¹ for commercial WC products andthose synthesized by other methods, the m-NRTC synthesized according tothe present invention has a high specific surface area of 198 m² g⁻¹, orat least 170 m² g⁻¹. This high surface area and uniformnanorod-structure of the synthesized m-NRTC makes it possible for it tobe used as a catalyst or o catalytic support in proton exchange membranefuel cells and direct methanol fuel cells.

The as-prepared electro-catalyst composed of Pt nanoparticles supportedon m-NRTC demonstrates higher electro-catalytic activity for methanolelectro-oxidation, better tolerance to CO poisoning and superiorperformance for the cathodic electrocatalytic hydrogen evolution than aPt/C catalyst.

As an extension, this work provides a simple and economic thought tosynthesize nanorod-structured WC materials by preparing precursors withthe desired external morphology, thus leading to more applications ofthose materials in the related reaction systems.

Whilst there has been described in the foregoing description exemplaryembodiments of the present invention, it will be understood by thoseskilled in the technology concerned that many variations in details ofdesign, construction and/or operation may be made without departing fromthe present invention. For example, other metal nanostructures such asnanoparticles of Pd, Ag, Rh may be deposited on the synthesizednanorod-structured WC materials for other catalysis applications.

REFERENCES

-   1. Levy, R. B.; Boudart, M., Platinum-Like Behavior of Tungsten    Carbide in Surface Catalysis. Science 1973, 181 (4099), 547-549.-   2. Vidick, B.; Lemaître, J.; Leclercq, L., Control of the catalytic    activity of tungsten carbides: III. Activity for ethylene    hydrogenation and cyclohexane dehydrogenation. Journal of Catalysis    1986, 99 (2), 439-448.-   3. Ledoux, M. J.; Huu, C. P.; Guille, J.; Dunlop, H., Compared    activities of platinum and high specific surface area Mo2C and WC    catalysts for reforming reactions: I. Catalyst activation and    stabilization: Reaction of n-hexane. Journal of Catalysis 1992, 134    (2), 383-398.-   4. Curry, K. E.; Thompson, L. T., Carbon-hydrogen bond activation    over tungsten carbide catalysts. Catalysis Today 1994, 21 (1),    171-184.-   5. Hwu, H. H.; Chen, J. G., Potential Application of Tungsten    Carbides as Electrocatalysts: 4. Reactions of Methanol, Water, and    Carbon Monoxide over Carbide-Modified W (110). The Journal of    Physical Chemistry B 2003, 107 (9), 2029-2039.-   6. Ribeiro, F. H.; Dalla Betta, R. A.; Boudart, M.; Baumgartner, J.;    Iglesia, E., Reactions of neopentane, methylcyclohexane, and    3,3-dimethylpentane on tungsten carbides: The effect of surface    oxygen on reaction pathways. Journal of Catalysis 1991, 130 (1),    86-105.-   7. Ribeiro, F. H.; Boudart, M.; Dalla Betta, R. A.; Iglesia, E.,    Catalytic reactions of n-Alkanes on [beta]-W2C and WC: The effect of    surface oxygen on reaction pathways. Journal of Catalysis 1991, 130    (2), 498-513.-   8. Weigert, E. C.; Stottlemyer, A. L.; Zellner, M. B.; Chen, J. G.,    Tungsten Monocarbide as Potential Replacement of Platinum for    Methanol Electrooxidation. The Journal of Physical Chemistry C 2007,    111(40), 14617-14620.-   9. Harnisch, F.; Schröder, U.; Quaas, M.; Scholz, F.,    Electrocatalytic and corrosion behaviour of tungsten carbide in    near-neutral pH electrolytes. Applied Catalysis B: Environmental    2009, 87 (1-2), 63-69.-   10. Nie, M.; Shen, P. K.; Wu, M.; Wei, Z.; Meng, H., A study of    oxygen reduction on improved Pt—WC/C electrocatalysts. Journal of    Power Sources 2006, 162 (1), 173-176.-   11. Santos, L.; Freitas, K.; Ticianelli, E., Electrocatalysis of    oxygen reduction and hydrogen oxidation in platinum dispersed on    tungsten carbide in acid medium. Journal of Solid State    Electrochemistry 2007, 11 (11), 1541-1548.-   12. Esposito, D. V.; Dobson, K. D.; McCandless, B. E.; Birkmire, R.    W.; Chen, J. G., Comparative Study of Tungsten Monocarbide and    Platinum as Counter Electrodes in Polysulfide-Based    Photoelectrochemical Solar Cells. Journal of The Electrochemical    Society 2009, 156 (8), B962-B969.-   13. Wang, Y.; Song, S.; Maragou, V.; Shen, P. K.; Tsiakaras, P.,    High surface area tungsten carbide microspheres as effective Pt    catalyst support for oxygen reduction reaction. Applied Catalysis B:    Environmental 2009, 89 (1-2), 223-228.-   14. Nie, M.; Shen, P. K.; Wei, Z., Nanocrystalline tungsten carbide    supported Au—Pd electrocatalyst for oxygen reduction. Journal of    Power Sources 2007, 167 (1), 69-73.-   15. Meng, H.; Shen, P. K., Tungsten Carbide Nanocrystal Promoted    Pt/C Electrocatalysts for Oxygen Reduction. The Journal of Physical    Chemistry B 2005, 109 (48), 22705-22709.-   16. Chhina, H.; Campbell, S.; Kesler, O., High surface area    synthesis, electrochemical activity, and stability of tungsten    carbide supported Pt during oxygen reduction in proton exchange    membrane fuel cells. Journal of Power Sources 2008, 179 (1), 50-59.-   17. Zhao, Z.; Fang, X.; Li, Y.; Wang, Y.; Shen, P. K.; Xie, F.;    Zhang, X., The origin of the high performance of tungsten    carbides/carbon nanotubes supported Pt catalysts for methanol    electrooxidation. Electrochemistry Communications 2009, 11 (2),    290-293.-   18. Chhina, H.; Campbell, S.; Kesler, O., Ex situ Evaluation of    Tungsten Oxide as a Catalyst Support for PEMFCs. Journal of The    Electrochemical Society 2007, 154 (6), B533-B539.-   19. Liu, N.; Kourtakis, K.; Figueroa, J. C.; Chen, J. G., Potential    application of tungsten carbides as electrocatalysts: III. Reactions    of methanol, water, and hydrogen on Pt-modified C/W (111) surfaces.    Journal of Catalysis 2003, 215 (2), 254-263.-   20. Hwu, H. H.; Chen, J. G., Potential application of tungsten    carbides as electrocatalysts. Journal of Vacuum Science & Technology    A: Vacuum, Surfaces, and Films 2003, 21 (4), 1488-1493.-   21. Xiao, T.; Hanif, A.; York, A. P. E.; Sloan, J.; Green, M. L. H.,    Study on preparation of high surface area tungsten carbides and    phase transition during the carburisation. Physical Chemistry    Chemical Physics 2002, 4 (14), 3522-3529.-   22. Brady, C. D. A.; Rees, E. J.; Burstein, G. T., Electrocatalysis    by nanocrystalline tungsten carbides and the effects of codeposited    silver. Journal of Power Sources 2008, 179 (1), 17-26.-   23. Welham, N. J., Formation of micronised WC from scheelite    (CaWO4). Materials Science and Engineering: A 1998, 248 (1-2),    230-237.-   24. Oxley, J. D.; Mdleleni, M. M.; Suslick, K. S.,    Hydrodehalogenation with sonochemically prepared Mo2C and W2C.    Catalysis Today 2004, 88 (3-4), 139-151.-   25. Zeng, D.; Hampden-Smith, M. J., Room-temperature synthesis of    molybdenum and tungsten carbides, Mo2C and W2C, via chemical    reduction methods. Chemistry of Materials 1992, 4 (5), 968-970.-   26. Wanner, S.; Hilaire, L.; Wehrer, P.; Hindermann, J. P.; Maire,    G., Obtaining tungsten carbides from tungsten bipyridine complexes    via low temperature thermal treatment. Applied Catalysis A: General    2000, 203 (1), 55-70.-   27. Gao, L.; Kear, B. H., Synthesis of nanophase WC powder by a    displacement reaction process. Nanostructured Materials 1997, 9    (1-8), 205-208.-   28. Tsuji, M.; Hashimoto, M.; Nishizawa, Y.; Kubokawa, M.; Tsuji,    T., Microwave-Assisted Synthesis of Metallic Nanostructures in    Solution. Chemistry—A European Journal 2005, 11 (2), 440-452.-   29. Liu, Z., Positive periodic solution for a neutral delay    competitive system. Journal of Mathematical Analysis and    Applications 2004, 293 (1), 181-189.-   30. Sun, S.; Jaouen, F.; Dodelet, J.-P., Controlled Growth of Pt    Nanowires on Carbon Nanospheres and Their Enhanced Performance as    Electrocatalysts in PEM Fuel Cells. Advanced Materials 2008, 20    (20), 3900-3904.-   31. Davis, R. J.; Derouane, E. G., A non-porous supported-platinum    catalyst for aromatization of n-hexane. Nature 1991, 349 (6307),    313.-   32. Lytle, J. C.; Denny, N. R.; Turgeon, R. T.; Stein, A.,    Pseudomorphic transformation of inverse opal tungsten oxide to    tungsten carbide. Advanced Materials 2007, 19 (21), 3682-+.-   33. F. Zhao, F. Harnisch, U. Schröder, F. Scholz, P. Bogdanoff    and I. Herrmann, Environmental Science & Technology, 2006, 40,    5193-5199.-   34. A. Contreras, R. Guirado and T. N. Veziroglu, International    Journal of Hydrogen Energy, 2007, 32, 4635-4640.-   35. A. Midilli and I. Dincer, International Journal of Hydrogen    Energy, 2007, 32, 511-524.-   36. W.-F. Chen, K. Sasaki, C. Ma, A. I. Frenkel, N.    Marinkovic, J. T. Muckerman, Y. Zhu and R. R. Adzic, Angewandte    Chemie International Edition, 2012, 51, 6131-6135.-   37. D. J. Ham, R. Ganesan and J. S. Lee, International Journal of    Hydrogen Energy, 2008, 33, 6865-6872.-   38. T. F. Jaramillo, J. Bonde, J. Zhang, B.-L. Ooi, K. Andersson, J.    Ulstrup and I. Chorkendorff, The Journal of Physical Chemistry C,    2008, 112, 17492-17498.-   39. Y. Li, H. Wang, L. Xie, Y. Liang, G. Hong and H. Dai, Journal of    the American Chemical Society, 2011, 133, 7296-7299.-   40. H. Vrubel, D. Merki and X. Hu, Energy & Environmental Science,    2012, 5, 6136-6144.-   41. Z. Wu, B. Fang, A. Bonakdarpour, A. Sun, D. P. Wilkinson and D.    Wang, Applied Catalysis B: Environmental, 2012, 125, 59-66.-   42. Z. Chen, D. Cummins, B. N. Reinecke, E. Clark, M. K. Sunkara    and T. F. Jaramillo, Nano Letters, 2011, 11, 4168-4175.-   43. A. Phuruangrat, D. J. Ham, S. Thongtem and J. S. Lee,    Electrochemistry Communications, 2009, 11, 1740-1743.

1. A method of synthesizing tungsten carbide nanorods, the methodcomprising: mixing tungsten oxide (WO₃) nanorods with a carbon source toobtain precursors; and calcining the precursors to obtain tungstencarbide nanorods, without use of any catalyst, wherein the carbon sourcecomprises glucose and the mixing comprises forming a mixture of tungstenoxide WO₃ nanorods with the glucose, the method further comprisinghydrothermally treating the mixture and evaporating the hydrothermallytreated mixture prior to the calcining, or wherein the carbon sourcecomprises methane and the mixing comprises heating the tungsten oxideWO₃ nanorods in the presence of the methane and hydrogen in a furnace.2. (canceled)
 3. The method of claim 1, wherein the hydrothermallytreating is performed in an autoclave at about 110° C. to 300° C. forabout 4 to 12 hours.
 4. (canceled)
 5. The method of claim 1, wherein thecalcining comprises heating the precursors at about 600° C. to 1000° C.under a flow of gas comprising at least one of: hydrogen and argon forabout 1 to 6 hours, wherein the gas comprises hydrogen and argon havinga respective volume ratio of 1:3 and wherein the flow of gas is at arate of about 300 mL/min. 6-8. (canceled)
 9. The method of claim 1,wherein the molar ratio of tungsten to carbon in the mixture is 0.078.10. The method of claim 1, wherein the precursors comprise carbon-coatedtungsten oxide (WO₃) nanorods.
 11. (canceled)
 12. Tungsten carbidenanorods synthesized according to the method of claim
 1. 13. Thetungsten carbide nanorods of claim 12, having a mesoporous structure.14. The tungsten carbide nanorods of claim 12, having a specific surfacearea greater than or equal to 170 m² g⁻¹.
 15. A method of synthesizing acatalyst of metal nanostructures supported on tungsten carbide nanorods,the method comprising: mixing tungsten oxide (WO₃) nanorods and a carbonsource to obtain precursors; calcining the precursors to obtain tungstencarbide nanorods, without use of any catalyst; and depositing metalnanostructures on the tungsten carbide nanorods to form the catalyst,wherein the metal nanostructures comprise platinum nanoparticles andwherein the depositing comprises: suspending the tungsten carbidenanorods in ethylene glycol to form a solution; addinghexachloroplatinic acid to the solution; and drying a solid in thesolution to form the catalyst.
 16. (canceled)
 17. The method of claim15, wherein suspending the tungsten carbide nanorods in ethylene glycolcomprises ultrasonic stirring.
 18. The method of claim 15, wherein thehexachloroplatinic acid is added dropwise to the solution to reach aconcentration of 4.6 mg platinum per millilitre of ethylene glycol. 19.(canceled)
 20. The method of any one of claim 15, further comprisingfiltering and washing the solid prior to the drying, wherein the dryingis performed in a vacuum oven at about 25° C. to 100° C.
 21. (canceled)22. The method of any one of claims 16 to 21, further comprisingincreasing alkalinity of the solution prior to the drying, whereinincreasing alkalinity comprises adding sodium hydroxide to adjust the pHof the solution to above
 13. 23. The method of any one of claims 16 to22, further comprising heating the solution to reduce platinum in thesolution prior to the drying, wherein the heating is at about 100° C. to200° C.
 24. (canceled)
 25. The method of claim 15, further comprisingpromoting with a sedimentation promoter adsorption of suspended platinumnanoparticles onto the tungsten carbide nanorods prior to the drying.26. The method of claim 15, wherein the metal nanostructures comprise atleast one selected from the group consisting: of Pd, Ag and Rh.
 27. Acatalyst of metal nanostructures supported on tungsten carbide nanorods,wherein each metal nanostructure is about 4 nm in average size.
 28. Thecatalyst of claim 27, wherein the metal nanostructures comprise platinumnanoparticles and wherein the catalyst is synthesized according to themethod of claim
 15. 29. The catalyst of claim 27, having a mesoporousnanorod structure comprising mesopores among aggregated nanorods. 30.The catalyst of claim 28, having a higher electro-catalytic activity formethanol electro-oxidation and having a greater tolerance to carbonmonoxide poisoning than a catalyst of platinum nanoparticles on a carbonsupport.
 31. (canceled)